1.2562 142W12 Cold Work Tool Steel

Categories	Tool Steel Bars
Brand	fushun
Model	1.2562 142W12
Process	hot rolled or hot forged
Delivery Condtion	annealed
Surface Condition	smooth, bright
FOB port	Shanghai
Terms of Payment	L/C, T/T
Update Time	Apr 28,2024

Contact Now

Favorites

Detail Information

1.2562 142W12 Cold Work Tool Steel

Description

Low alloyed W cold working tool steel.The high quality Germany DIN 1.2562 material is one of the more steel grades we supply, Alloyed WV steel.

Applications

Cutting tools, stamping, woodworking, drawing, deep drawing and pressing tools, cold working rolls, measuring tools.

Chemical Composition (in weight %)

Grade	C	Si	Mn	Cr	V	W
1.2562	1.43	0.23	0.30	0.35	0.25	3.05

Mechanical Properties of 1.2562

Rp0.2 (MPa)

Rm (MPa)

Impact

KV (J)

Elongation

A (%)

A Z (%)

Delivery

Hardness HB

715 (≥)

459 (≥)

31

34

23

Solution & Aging, Ann, Ausaging, Q+T

314

Soft Annealing

Heat to 720-750℃, cool slowly in furnace. This will produce a maximum Brinell hardness of 270.

Stress Relieving

Stress relieving to remove machining stresses should be carried out by heating to approx. 650℃, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.

Hardening

Harden from a temperature of 800-830℃ followed by water quenching. Hardness after quenching is 66 HRC.

Tempering

Tempering temperature: 100-250℃.

Forging

Hot forming temperature: 1050-850℃.