40CrNiMoA Alloy Steel Bar
| Categories | Alloy Steel Bars |
|---|---|
| Brand | fushun |
| Model | 40CrNiMoA |
| Delivery Condition | normalised and tempered/softened |
| Update Time | Apr 30,2025 |
40CrNiMoA Steel
40CrNiMoA steel is a Chinese alloy steel, has high strength, toughness and good hardenability, and has anti-overheating stability, but has high white point sensitivity, temper brittleness and poor weldability. Preheating is required before welding, and stress relief treatment is required after welding.
Properties and Applications of 40CrNiMoA Alloy Steel
40CrNiMoA steel is used after quenching and tempering, and is used to manufacture important parts requiring good plasticity, high strength and large size. For example, heavy-duty shafts in heavy-duty machines, steam turbine shafts with diameters greater than 250 mm, blades, transmissions, fasteners, crankshafts, gears, etc., can also be used for rotor shafts and blades operating at temperatures exceeding 400 °C.
40CrNiMo, 40CrNiMoA Steel Chemical Composition
Steel Grade | C | Si | Mn | P | S | Cr | Ni | Mo | Cu |
|---|---|---|---|---|---|---|---|---|---|
40CrNiMo | 0.37 to 0.44 | 0.17 to 0.37 | 0.50 to 0.80 | ≤ 0.020 to ≤ 0.030 | ≤ 0.010 to ≤ 0.030 | 0.60 to 0.90 | 1.25 to 1.65 | 0.15 to 0.25 | ≤ 0.25 to ≤ 0.30 |
40CrNiMoA Alloy Steel Mechanical Properties
Yield strength: ≥ 835 MPa
Tensile strength: ≥ 980 MPa
Elongation: ≥12%
Rate of reduction in area: ≥55%
Impact absorbing energy: ≥ 78 J
Material Brinell Hardness: ≤ 269 (Annealed or high temperature tempered steel rod)
Sample size: 25mm
Heat treatment specification
First quenching heating temperature: 850 °C (Quenchant– oil)
Tempering heating temperature: 600 °C (Quenchant– water, oil)
- Tel
- *Title
- *Content
- Name:
- Florence Tang
- Tel:
86-731-89903933
- Address:
- ADD: No. 812-813, Floor 8, Building C2, Yongsheng Commercial Plaza, 222 Labor East Road, Yuhua District, Changsha City, Hunan, China.
sign up for the latest catalogue, new design and promotion
Mobile WEB