DIN 1.7185 33MnCrB5-2 Alloy Steel Round Bars

Categories	Hardened Steel Bar
Brand	fushun
Model	1.7185
Diameter	50-260mm
Delivery condition	Hot forged, Hot rolled, QT
Surfac condition	Black, bright
FOB port	Shanghai
Terms of Payment	L/C, T/T
Update Time	Apr 30,2025

Contact Now

Favorites

Detail Information

Introduction of 1.7182 steel:

Hot rolled Hardenable Steel has been developed to be hardened, either by heat treatment after workshop processing, or by a direct hot forming & quenching process to get their final properties. Hardenable Steel is a perfect base material for a great variety of products, parts and components, that need extreme hardness, wear resistance, high strength, toughness and resistance to mechanical load. These Hardenable Steel properties after heat treatment ensure longer lifetime and considerable weight reduction. Good forming- bending- welding- and cutting properties enable the manufacturing of complicated structures, components and parts.

Application of 1.7182 steel:

Wear plates, Grader blades, Track shoes, Liner plates, Screen plates, Crushers, Knives, Saw blades, Spades, Hand tools, Ploughs, Discs for harrows, Washers, Safety parts and components

Chemical Composition of 1.7182 steel:

Steel Grade	C	SI	MN	P	S	CR	B
1.7185	0.30-0.36	0.4MAX	1.2-1.5	0.025MAX	0.035MAX	0.3-0.6	0.0008-0.0050

Mechanical Property of 1.7182 steel:

Steel Grade	Thickness (mm)	Yield Strength (MPA)	Tensile Strength (MPA)	Elongation (%)
1.7185	3	850 min	1050-1300	13 min
1.7185	8	800 min	950-1200	13 min