DIN 1.2436 D6 SKD2 Hot Forged Tool Steel Bar

DIN 1.2436 D6 SKD2 Hot Forged Tool Steel Bar

DIN 1.2436 D6 SKD2 Hot Forged Tool Steel Bar
DIN 1.2436 D6 SKD2 Hot Forged Tool Steel BarDIN 1.2436 D6 SKD2 Hot Forged Tool Steel Bar
CategoriesRound Forgings
Brandfushun
Model1.2436
Diameter200-550mm
Surface conditionBlack, Grinded, Peeled
Delivery ConditionHot forged+annealed
FOB portHuangshi,Shanghai
Terms of PaymentL/C, T/T
Update TimeMar 29,2024
Detail Information

Introduction:

DIN1.2436 tool steel is a high-carbon, high chromium tool steel alloyed with tungsten that is characterized by high compressive strength, high wear resistance, high surface hardness and good hardening stability.

Applications:

Typical applications for DIN1.2436 tool steel include blanking and shearing tools, drawing tools, drawing dies, mandrels, press tools, forming tools and shear blades. DIN1.2436 tool steel is suited to applications where maximum wear resistance is required.

Standard

Chemical Composition:

Grade

C

Mn

P

S

Si

Cr

W

1.2436

2.00-2.30

0.60 max

0.030 max

0.030 max

0.60 max

11.00-
13.50

0.60-
0.90

Delivery Condition:

Similar Grade: DIN1.2436, D6,SKD2

Shape: Round, Flat, Square.

Size Range:Dia60-500mm

 
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR

Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Heat Treatment:

FORGING: Heat the DIN1.2436 tool steel slowly and uniformly to 700°C then more rapidly to 900-1050°C. After forging cool slowly, preferably in a furnace.
ANNEALING: DIN1.2436 tool steel is supplied in the annealed and machineable condition. Re-annealing will only be necessary if the tool steel has been forged or hardened by the toolmaker. To anneal heat to 800-840°C and slow furnace cool. Hardness after annealing will be approximately 225 brinell.
STRESS RELIEVING: If machining operations have been heavy or if the tool has an unbalanced section, remove stresses before hardening by heating up to 650-700°C, equalise, then cool slowly.
HARDENING: Pre heat slowly to 750-800°C and thoroughly soak. Continue heating to the final hardening temperature of 950-980°C and allow the component to be heated through. Cool in air or quench in oil. D6 is suitable for vacuum (high speed gas) hardening.
TEMPERING: To temper heat uniformly and thoroughly at the selected tempering temperature and hold for at least one hour per 25mm of total thickness. Double tempering should be carried out with intermediate cooling to room temperature.

Please send your message to us
*Email
Tel
*Title
*Content
Upload
  • Only supports .rar/.zip/.jpg/.png/.gif/.doc/.xls/.pdf, maximum 20MB.
CONTACT PERSON
Name:
Florence Tang
Tel:

86-731-89903933

Email:
Address:
ADD: No. 812-813, Floor 8, Building C2, Yongsheng Commercial Plaza, 222 Labor East Road, Yuhua District, Changsha City, Hunan, China.
NEWSLETTER

sign up for the latest catalogue, new design and promotion

follow us