4145H MOD Forged Machined Alloy Steel Stabilizer

4145H MOD Forged Machined Alloy Steel Stabilizer

4145H MOD Forged Machined Alloy Steel Stabilizer
CategoriesSteel Forgings
Brandfushun
Model4145H,4145H-MOD
Diameter200-800mm
Steel grade4145h,4145h-mod
Delivery conditionForged
Surface conditionBright, black
FOB portShanghai
Terms of PaymentL/C, T/T
Update TimeMar 29,2024
Detail Information

Applications

AISI 4145H MOD Steel is commonly used for a variety of applications in the oil and gas sector. Used often for the manufacture of down hole drilling tools such as drill collars. Other applications include gears, shafts for hydraulic presses, rolls for paper mills, pump shafts and tool holders.

Description

AISI 4145H MOD is a chromium molybdenum quality alloy steel specification. As a high tensile steel grade AISI 4145H MOD is primarily supplied in the hardened and tempered condition to 30-36HRc range to AISI 4145H MOD. With a slightly higher carbon content AISI 4145H MOD is similar to AISI 4140 in that it offers good ductility, shock resisting characteristics combined with resistance to wear.

Chemical Composition(%)

C

Mn

Si

P

S

Cr

Ni

Mo

0.43-0.49

0.85-1.10

0.10-0.35

0.035 max

0.040 max

0.80-1.10

0.25 max

0.15-0.25

Mechanical Property Requirements

Tensile Strength Rm (KSI)

Yield Strength R2 (KSI)

Elongation(%)

Reduction Ration (%)

Hardness (HRC)

140 min

120 min

14 min

40 min

30-36

HEAT TREATMENT

Heat treatment temperatures, including rate of heating, cooling and soaking times will vary due to factors such as the shape and size of eachAISI 4145H MOD Steel component. 

Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities.

 Please consult your heat treatment provider for full guidance on heat treatment of AISI 4145H MOD Steel.


Annealing: Heat the steel slowly to 800-850°C and allow enough time for the steel to be thoroughly heated. Cool slowly in the furnace to 480°C followed by air cooling.

Stress Relieving: When parts are heavily machined, ground or otherwise subject to cold work, stress relieving will be beneficial prior to hardening.

Hardening: AISI 4145H MOD Steel is usually supplied ready heat treated to 30-36HRc. If further heat treatment is required annealed AISI 4145H MOD Steel should be heated slowly to 840-875°C and after adequate soaking at this temperature quench in oil. Temper as soon as the tools reach room temperature.


Tempering: Heat carefully to a suitable temperature selected by reference to a tempering chart or table (usually between 550-700°C, soak at the temperature for 2 hours per 25mm of ruling section, then allow to cool in air. Tempering between 250-375°C is not advised as tempering within this range will seriously reduce the impact values of this steel.

4145h steel
Please send your message to us
*Email
Tel
*Title
*Content
Upload
  • Only supports .rar/.zip/.jpg/.png/.gif/.doc/.xls/.pdf, maximum 20MB.
CONTACT PERSON
Name:
Florence Tang
Tel:

86-731-89903933

Email:
Address:
ADD: No. 812-813, Floor 8, Building C2, Yongsheng Commercial Plaza, 222 Labor East Road, Yuhua District, Changsha City, Hunan, China.
NEWSLETTER

sign up for the latest catalogue, new design and promotion

follow us