DIN 1.6510 39NiCrMo3 Quenched and Tempered Steel Bars

DIN 1.6510 39NiCrMo3 Quenched and Tempered Steel Bars

DIN 1.6510 39NiCrMo3 Quenched and Tempered Steel Bars
CategoriesHardened Steel Bar
Brandfushun
Model1.6510
Diameter50-550mm
Similar steel gradeDIN1.6510, 39NiCrMo3, 36CrNiMo4, AISI9840
Delivery conditionHot forged, Hot rolled, QT
Surfac conditionBlack, bright
FOB portShanghai
Terms of PaymentL/C, T/T
Update TimeMar 29,2024
Detail Information

Application of 1.6510 steel:

The steel is suited to production of highly stressed components of large cross section for aircraft, automotive and general engineering applications, such as forged propeller shafts, connecting rods, gear shafts, crankshafts and landing gear components.

Chemical Composition of 1.6510 steel(%)

C

Mn

Si

P

S

Cr

Ni

Mo

0.35-0.43

0.50-0.80

0.40 max

0.025 max

0.035 max

0.80-1.10

0.70-1.00

0.15-0.25

Heat treatment of 1.6510 steel:

Annealing: Austenitize at 1525ºF (830ºC) and slow cool from 1280 to 1200ºF (iso anneal) to give coarse pearlite structure for optimum machinability.

Normalizing: At 1600ºF (870ºC) followed by air cool.

Hardening: from 1525-1575ºF (830-860ºC) and oil quench for thin, intricate shapes, water quench for large, simple shapes.

Tempering: from 1000-1250ºF(540-680ºC) as per required properties.

Machinability of 1.6510 steel:

The steel may be readily machined, preferably from a coarse pearlitic structure.

Weldability of 1.6510 steel:

Pre-heat and post-weld stress relief are recommended for welding of this alloy. Welding should not be carried out in the hardened and tempered condition.

Please send your message to us
*Email
Tel
*Title
*Content
Upload
  • Only supports .rar/.zip/.jpg/.png/.gif/.doc/.xls/.pdf, maximum 20MB.
CONTACT PERSON
Name:
Florence Tang
Tel:

86-731-89903933

Email:
Address:
ADD: No. 812-813, Floor 8, Building C2, Yongsheng Commercial Plaza, 222 Labor East Road, Yuhua District, Changsha City, Hunan, China.
NEWSLETTER

sign up for the latest catalogue, new design and promotion

follow us