AISI 4140 G41400 1.7225 42CrMo4 SCM440 Quenched Tempered Alloy Steel Round Bar

AISI 4140 G41400 1.7225 42CrMo4 SCM440 Quenched Tempered Alloy Steel Round Bar

AISI 4140 G41400 1.7225 42CrMo4 SCM440 Quenched Tempered Alloy Steel Round Bar
CategoriesHardened Steel Bar
Brandfushun
Model4140 G41400 1.7225 42CrMo4 SCM440
Diameter30-300mm
Surface ConditionBlack, Peeled
Delivery conditionQuenched+Tempered
FOB portShanghai, Tianjin
Terms of PaymentL/C, D/A, D/P, T/T
Update TimeMar 29,2024
Detail Information
Introduce of 4140 Steel

AISI 4140 steel is a low alloy steel containing chromium, molybdenum, and manganese. It is widely used across numerous industries and is an excellent material choice due to its toughness, high fatigue strength, and abrasion and impact resistance. Not many grades can match the versatility and usefulness of 4140.
Applications of 4140 Steel
This alloy finds many applications as forgings for the aerospace and oil and gas industries, along with myriad uses in the automotive, agricultural and defense industries, Typical uses are forged gears and shafts, spindles, fixtures, jigs and collars.

Chemical Composition(%):

Grade

C

Si

Mn

P

S

Cr

Mo

42CrMo4

0.38- 0.45

0.40

max

0.60-

0.90

0.025

max

0.035 max

0.90- 1.20

0.15- 0.30

Mechanical Property

Grade
42CrMo4 Mechanical Property
Thickness
Yield
Tensile
Elongation
42CrMo4
mm
Min Mpa
Mpa
Min %
3<t≦8
900
1100-1300
10
8<t≦20
750
1000-1200
11
20<t≦60
650
900-1100
12
60<t≦100
550
800-950
13
100<t≦160
500
750-900
14
Heat Treatment of 4140 Steel
AISI 4140 alloy steel is heated at 845°C (1550°F) followed by quenching in oil. Before hardening, it can be normalized by heating it at 913°C (1675°F) for a long period of time, followed by air cooling.

Annealing of 4140 Steel
AISI 4140 alloy steel is annealed at 872°C (1600°F) followed by slowly cooling in the furnace.

Tempering of 4140 Steel
AISI 4140 alloy steel can be tempered at 205 to 649°C (400 to 1200°F) depending upon the desired hardness level. The hardness of the steel can be increased if it has a lower tempering temperature. For example, a tensile strength of 225 ksi can be achieved by tempering at 316°C (600°F), and tensile strength of 130 ksi can be achieved by tempering at 538°C (1000°F).

Hardening of 4140 Steel
AISI 4140 alloy steel can be hardened by cold working, or heating and quenching.
Machinability
Machinability of 4140 Steel
AISI 4140 alloy steel has good machinability in the annealed condition.

Forming of 4140 Steel
AISI 4140 alloy steel has high ductility. It can be formed using conventional techniques in the annealed condition. It requires more pressure or force for forming because it is tougher than plain carbon steels.

Welding of 4140 Steel
AISI 4140 alloy steel can be welded using all conventional techniques. However, the mechanical properties of this steel will be affected if it is welded in the heat-treated condition, and post-weld heat treatment should be performed.
4140 steel
Please send your message to us
*Email
Tel
*Title
*Content
Upload
  • Only supports .rar/.zip/.jpg/.png/.gif/.doc/.xls/.pdf, maximum 20MB.
CONTACT PERSON
Name:
Florence Tang
Tel:

86-731-89903933

Email:
Address:
ADD: No. 812-813, Floor 8, Building C2, Yongsheng Commercial Plaza, 222 Labor East Road, Yuhua District, Changsha City, Hunan, China.
NEWSLETTER

sign up for the latest catalogue, new design and promotion

follow us